Enhanced visible light absorption in layered Cs3Bi2Br9 through mixed-valence Sn(II) / Sn(IV) doping

Lead-free halides with perovskite-related structures, such as the vacancy-ordered perovskite Cs3Bi2Br9, are of interest for photovoltaic and optoelectronic applications. Addition of SnBr2 to the solution-phase synthesis of Cs3Bi2Br9 leads to substitution of up to 7% of the Bi(III) ions by equal quantities of Sn(II) and Sn(IV). The resulting mixed-valence compounds show intense visible and near infrared absorption due to intervalence charge transfer, intermediate band transitions. Sn(II) and Sn(IV) defects occupy neighbouring B-cation sites, forming a double-substitution complex. Unusually for a Sn(II) compound, the material shows minimal changes in optical and structural properties after 12 months storage in air. Our calculations suggest the stabilisation of Sn(II) within the double substitution complex contributes to this unusual stability. These results expand upon research on inorganic mixed-valent halides to a new, layered structure, and offer insights into the tuning, doping mechanisms, and structure-property relationships of lead-free vacancy-ordered perovskite structures.